Coercive field in Sm2Fe17Nx hydrogen decrepitated magnets

The coercivity mechanism of Sm2Fe17Nx hydrogen decrepitated magnets is analysed on the basis of micromagnetism. The discrepancy between the experimentally realized coercivity and the ideal nucleation field as predicted by Brown is also found in Sm2Fe17Nx magnets. This discrepancy is due to the effect of the microstructure. Our analysis strongly indicates that the coercivity in Sm2Fe17Nx hydrogen decrepitated magnets is controlled by the nucleation mechanism. The anisotropy constants K1, K2, and the saturation polarization Js of Sm2Fe17Nx in the temperature range from 200 to 620 K are determined from the analysis of the approach to ferromagnetic saturation. Der Koerzitivfeldmechanismus von durch Wasserstoffversprodung hergestellten Sm2Fe17Nx-Magneten wird unter Zugrundelegung der Theorie des Mikromagnetismus analysiert. Der Unterschied zwischen den experimentell festgestellten Koerzitivfeldstarken und dem von Brown vorhergesagten idealen Keimbildungsfeld wird auch im Falle der Sm2Fe17Nx-Magnete beobachtet. Dieser Unterschied wird auf die Rolle der Mikrostruktur zuruckgefuhrt. Unsere Analyse gibt starke Hinweise darauf, das das Koerzitivfeld in durch Wasserstoffversprodung hergestellten Sm2Fe17Nx-Magneten durch einen Keimbildungsmechanismus bestimmt ist. Im Temperaturbereich von 200 bis 620 K werden die Anisotropiekonstanten K1, K2 und die Sattigungspolarisation von Sm2Fe17Nx mit Hilfe einer Analyse der Einmundung in die ferromagnetische Sattigung bestimmt.