Extreme sensitivity of magnetic properties on the synthesis routes in La0.7Sr0.3MnO3

La0.7Sr0.3MnO3 polycrystalline samples have been prepared using different synthesis routes. X-ray Diffraction (XRD) confirms that the samples are of single phase with R-3c space group. The surface morphology and particle size has been observed using Field Emission Scanning Electron Microscopy (FESEM). Magnetic measurement shows that the magnetization in the materials are affected by low crystallite size which destroys the spin ordering due to strain at grain boundaries and this also leads to reduction in magnetization as well as high coercivity in the material.