Controls on the formation of Fe(II,III) (hydr)oxides by Fe(0) electrolysis
2018
Abstract This study identifies the electrochemical and solution chemical controls on the production of Fe(II,III) (hydr)oxides formed by the electrolysis of Fe(0) metal, also knows as Fe(0) electrocoagulation. EXAFS spectroscopy and X-ray diffraction were used to characterize the solids produced as a function of: i) applied current, which corresponded to iron(II) production rates of 30–300 μM min −1 , ii) pH and iii) background electrolyte. Two systems were investigated where: i) the dissolved oxygen (O 2 ) concentration was maintained at 0.1, 0.3 and 3.0 mg L −1 and ii) the O 2 drifted in response to varied Fe(II) addition rates. A narrow range of O 2 separated the domains for Fe(II,III) and Fe(III) (hydr)oxide formation. At O 2 ≥ 0.3 mg L −1 , Fe(III) solids dominated, while Fe(II,III) (hydr)oxides were the principal phases at O 2 = 0.1 mg L −1 . The highest fraction of Fe(II,III) (hydr)oxides formed in the O 2 drift experiments at the highest Fe(II) production rate, i.e. 300 μM min −1 . The background electrolyte determined the type of Fe(II,III) (hydr)oxide that formed: NaCl solutions favored magnetite and NaHCO 3 solutions favored carbonate green rust. Our results are consistent with an Fe(II,III) (hydr)oxide formation pathway where Fe(II) addition after O 2 depletion leads to rapid (
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
71
References
12
Citations
NaN
KQI