Estudio de la descomposición de fases durante el sinterizado por plasma de compósitos Al-5%Ni 3 Al
2019
The synthesis of Al-matrix composites reinforced with nanocrystalline intermetallic particles of Ni 3 Al was carried out with the Spark Plasma Sintering (SPS) technique. The Al-5%Ni 3 Al powder mixture was sintered by SPS at two different conditions: (i) 450 °C, 47 MPa and 180 s (4M47) and (ii) 520 °C, 16 MPa and 600 s (5M16). The Ni 3 Al particles were obtained by mechanical alloying after a milling time of 1260 ks. The composites show partial decomposition on the Ni 3 Al-Al interface, with the formation of the Al 3 Ni and Ni 2 Al 3 phases. The analysis by TEM confirms the nanometric characteristics of the Ni 3 Al particles in the composites. The sintered composites 4M47 and 5M16 presented 95% and 87% of the theoretical density and Vickers microhardness values of 62.3±7 and 55.3±5 HV respectively. Nanoindentation tests show that the mechanical properties of the Al 3 Ni, Al 3 Ni 2 and Ni 3 Al intermetallics are higher in high-pressure sintering conditions.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
34
References
0
Citations
NaN
KQI