Intermetallic RE6T5Al7 Phases (RE = Sc, Y, Ce–Nd, Sm, Gd–Lu; T = Ru, Ir): Diversity in their Magnetic, Magnetocaloric, and Critical Properties
2019
Over 20 new compounds of the RE6T5Al7 series (RE = Sc, Y, Ce–Nd, Sm, Gd–Lu; T = Ru, Ir; Yb6Ir5Ga7 type structure; superstructure of MgZn2; fully ordered Nb6.4Ir4Al7.6 type) have been synthesized. They crystallize in the hexagonal crystal system with space group P63/mcm. Their lattice parameters are in the ranges of a = 935–963 and c = 851–874 pm for the RE6Ru5Al7 and a = 913–966 and c = 825–865 pm for the RE6Ir5Al7 series. Four structures (Ho6Ru5Al7, Yb6Ru4.68(1)Al7.32(1), Sc6Ir5Al7, and Ho6Ir4.53(1)Al7.47(1)) have been refined from single-crystal data, indicating fully ordered structures for Ho6Ru5Al7 and Sc6Ir5Al7; however, T/Al mixing was observed on one crystallographic site for Ho6Ir4.53(1)Al7.47(1) and on two sites for Yb6Ru4.68(1)Al7.32(1). The Sc-, Y-, and Lu-containing compounds exhibit Pauli paramagnetism in line with a filled d band for Ru and Ir. Ce6Ru5Al7 exhibits mixed-valent behavior, while Yb6Ru5Al7 is solely trivalent. The other compounds exhibit paramagnetism and ferromagnetic phase tran...
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
61
References
3
Citations
NaN
KQI