Evaluations of the stability of sheathless electrospray ionization mass spectrometry emitters using electrochemical techniques

The processes that cause the failure of sheathless electrospray ionization (ESI) emitters, based on different kinds of gold coatings on fused-silica capillaries, are described and explained. The methods chosen for this study include electrochemical methods, ICPMS analysis of the electrolytes used, SEM studies, and electrospray experiments. Generally, the failure occurs by loss of the conductive coating. It is shown that emitters with sputter-coated gold lose their coatings because of mechanical stress caused by the gas evolution accompanying water oxidation or reduction. Emitters with gold coatings on top of adhesion layers of chromium and nickel alloy withstand this mechanical stress and have excellent durability when operating as cathodes. When operating as anodes, the adhesion layer is electrochemically dissolved through the gold film, and the gold film then flakes off. It is shown that the conductive coating behaves as a cathode even in the positive electrospray mode when the magnitude of a superimpos...