The Effect of Plume Generated on the Microstructural Behavior of the Weld Mixed Zone in High-Speed Laser Dissimilar Welding

Dissimilar laser welding has been researched to combine the excellent anticorrosion and high strength properties of Ti and the low weight and cost of Al. However, when welding dissimilar Al and Ti sheets, many kinds of intermetallic compound are easily generated. Therefore, intermetallic compounds and differences in material properties make joining such dissimilar metals very difficult. Previous studies clarified that ultra-high welding speed could suppress the weld defects. To elucidate the mechanism of Al and Ti dissimilar laser welding, material behavior of the weld fusion zone and components of fume generated during the ultra-high speed welding process were observed and analyzed using energy dispersive X-ray spectroscopy (EDX), transmission electron microscopy (TEM), high speed cameras, and a spectrometer. The results show that the atom movement of Al and Ti in the weld plume affects the behavior of elemental components distributed in the weld fusion zone.