Precipitation Reactions in 12Cr-3Ni-3Mn-3Cu-0.15Nb steel

2021 
Abstract In the current study, a new precipitation hardenable stainless steel was designed with primarily Ni and Mn modification using Thermo-Calc. The solution-annealing heat treatment at 1035 °C for 60 min followed by air quenching resulted in a fully martensitic microstructure. The as-quenched steel responded to the aging heat treatment, resulting in a significant enhancement of hardness and mechanical strength. The aging heat treatment at 500 °C for 120 min provided a good combination of tensile properties. The change in mechanical properties was quite conducive to the aging parameters (i.e., temperature and time) between 400 °C and 600 °C. Transmission electron microscopy and atom probe tomography studies demonstrated that the evolution of Cu-precipitate was the prime reason for the change in hardness and mechanical properties of as-quenched steel. As a result, the newly developed PH-1 steel was comparable to a commercial Cu-precipitate strengthened 17-4 PH steel in terms of mechanical properties. The Cu-precipitate evolved with a concurrent increase of Cu and decrease of Fe contents. APT studies revealed the interfacial segregation of Ni and Mn at the matrix and the Cu-rich precipitate in a peak-aged condition, which evolved as Ni-Mn rich reverse austenite upon over-aging, accompanied by high Mn:Si ratio. Cu precipitate only acted as a heterogeneous nucleation site for reverse austenite formation as there was no Cu atoms partition.
    • Correction
    • Source
    • Cite
    • Save
    • Machine Reading By IdeaReader
    59
    References
    3
    Citations
    NaN
    KQI
    []