Influence of annealing temperature on physical properties and photocatalytic ability of g-C3N4 nanosheets synthesized through urea polymerization in Ar atmosphere

Abstract The influences of annealing temperature on structure, morphology, vibration, optical properties and photocatalytic ability of g-C 3 N 4 nanosheets synthesized from urea in Ar atmosphere were investigated in detail by using x-ray diffraction (XRD) analysis, scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), Brunauer–Emmett–Teller (BET), Fourier transform infrared spectroscopy (FTIR), UV–vis absorption, and photoluminescence (PL). It was found that the preparation temperature had a great effect on structure and physical properties of g-C 3 N 4 . As the processing temperature increased from 450 °C to 650 °C, the interlayer stacking distance of g-C 3 N 4 decreased from 3.281 A to 3.217 A and the lattice parameter a decreased from 5.010 A to 4.934 A. This indicated a denser packing fashion of g-C 3 N 4 at high annealing temperature. Moreover, the FTIR spectra and SEM images revealed a large fraction of small polymer segments containing only a few heptazine units as annealing temperature increased. BET result indicated an increasing specific surface area as preparation temperature increased. UV–vis absorption spectra showed a decrease of the band gap energy with increasing calcination temperature which agrees well with the measured PL spectra. It was demonstrated that samples annealed at 550 °C exhibited the strongest photocatalytic activity. A decomposition of 80% and 100% of rhodamine B was obtained within respectively 1 h and 2 h under Xenon lamp irradiation. Photocatalytic result could be adequately explained based on evidences of specific surface area, average pore volume and pore size, and recombination rate of photoinduced electron-hole pairs.