Effect of temperature and dose on vacancy-defect evolution in 304L stainless steel irradiated by triple ion beam

Abstract This study aims to investigate the effects of temperature and dose on the vacancy-defect evolution in 304L stainless steel irradiated by the triple beam of Ni, H, and He ions below 673 K, which is relevant to water-cooled nuclear energy facilities. The irradiation experiments were performed simultaneously using 150-MeV Ni ions whose energy was degraded by passing through a tantalum foil of 8.5-μm thick, 100-keV H ions, and 200-keV He ions at 473, 523, 573, 623, and 673 K, respectively. The irradiation-induced microstructures in the steel were probed by the slow positron beam technique. The results show that the S parameter of the irradiated sample decreases as the temperature increases, and the S parameter of the high-dose irradiated sample decreases further. We explained the results by analyzing the structure of the defects in the irradiated samples at various temperatures and the effects of the annealing effect. In addition, the analysis of the S W plots reveals the transition of the helium-vacancy cluster to the overpressured He m V n (m > n) cluster under the influence of temperature and irradiation dose.