Preparation of waterborne dispersions of epoxy resin by ultrasonic-assisted supercritical CO2 nanoemulsification technique

Abstract Waterborne nanoemulsion of diglycidyl ether of bisphenol A type epoxy resin (DGEBA) with droplet size of around 124 nm was prepared by using an ultrasonic-assisted supercritical carbon dioxide (scCO 2 ) technique in an autoclave reactor at a low temperature (32 °C). A view cell positioned in-line with the ultrasonic probe allowed observation of the emulsification process. From the image analysis and droplet size measurement, the influence mechanisms of the ultrasonic power, the degree of mixing of scCO 2 with DGEBA, the adding amount of emulsifier, and the system pressure on emulsification process and emulsion droplet size were investigated. In the emulsification process, scCO 2 penetrated into the mixture and absorbed on the DGEBA molecular. The interactions between CO 2 and the functional groups of DGEBA reduced the chain-chain interactions of polymer segments and therefore efficiently reduced the viscosity of DGEBA at a low temperature. Meantime, the cavitation and acoustic streaming of ultrasound provided a shear force for the nanoemulsification and a disturbance force for the homogeneity of the emulsion. Therefore, the combination of scCO 2 and ultrasonication made it possible to prepare a long-term stable nanoemulsion under a low temperature. This ultrasonic-assisted scCO 2 emulsification method provides an efficient and solvent-free process for the preparation of waterborne nanoemulsions of, for example, some heat-sensitive and water-insoluble active substances at low temperature.