Preparation and characterization of pure rutile TiO 2 nanoparticles for photocatalytic study and thin films for dye-sensitized solar cells

Pure rutile-phase TiO2 (r-TiO2) was synthesized by a simple one pot experiment under hydrothermal condition using titanium (IV) n-butoxide as a Ti-precursor and HCl as a peptizer. The TiO2 products were characterized by XRD, TEM, ESCA, and BET surface area measurement. The r-TiO2 were rodlike in shape with average size of ∼61 × 32nm at hydrothermal temperature of 220°C for 10 h. Hydrothermal treatment at longer reaction time increased the tendency of crystal growth and also decreased the BET surface area. The degradation of methylene blue was selected as a test reaction to confer the photocatalytic activity of as-obtained r-TiO2. The results showed a strong correlation between the structure evolution, particle size, and photocatalytic performance of r-TiO2. Furthermore, the r-TiO2-based solar cell was prepared for the photovoltaic characteristics study, and the best efficiency of ∼3.16% was obtained.