Controlled synthesis of porous 3D interconnected MnO /C composite aerogel and their excellent lithium-storage properties
2019
Abstract To improve electrochemical performance of MnO electrodes, the porous 3D interconnected MnO/C composite aerogel is, at first, fabricated through direct carbonization of polyacrylic acid (PAA)-assisted manganese-based aerogel. Herein, the influences of carbonization temperature and the amount of PAA on the microstructure and lithium storage performance of composites are presented. MnO/C composite aerogel n3-550 (carbothermal reduction at 550 °C with the 30 mmol addition of PAA) shows the minimal MnO crystalline size, and the MnO/C composite aerogel n3-650 (carbothermal reduction at 650 °C with the 30 mmol addition of PAA) has the largest surface area and highest porosity. When evaluated as anodes for lithium ion batteries, the composite n3-550 exhibits the highest reversible capacity of 1081.8 mAh g −1 after 100 cycles at current density of 0.2 A g −1 , n3-650 electrode displays the most outstanding rate capability (601 mAh g −1 at 2 A g −1 ), and the highest coulombic efficiency (initial coulombic efficiency of 69.8% and greater than 98% after the 6th cycles). These excellent electrochemical performances are as a result of the porous interconnected 3D networks composited of hybridized nano-MnO with carbon, providing outstanding electrical conductivity and 3D charge transport channels. This facile and efficient strategy provides a horizon and deep understanding for advancing the design of high-performance oxide based anode materials.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
55
References
17
Citations
NaN
KQI