Synthesis and properties of crosslinked polyvinylformamide and polyvinylamine hydrogels in conjunction with silica particles

Polyvinylamine hydrogels with silica particles encapsulated (PVAm/silica) were produced by a two-step synthesis. In the first step, polyvinylformamide/silica (PVFA/silica) hybrids were synthesized from vinylformamide (VFA) and 1,3-divinylimidazolidin-2-one (1,3-bisvinylethyleneurea, BVU), as the crosslinker, by radical copolymerization in silica/water suspensions using different compositions of VFA/BVU. The target product PVAm/silica was obtained by acidic hydrolysis of the PVFA/silica hydrogels in a second step. The chemical structures of both hydrogels, PVFA/silica and PVAm/silica, respectively, were revealed by solid-state 13C(1H) cross-polarity/magic-angle spinning NMR spectroscopy. Both hydrogels swelled significantly in water. The swelling capacity of the two systems was characterized by the correlation length ξ (or hydrodynamic blob size) of the network meshes with small-angle neutron scattering experiments. ξ is significantly larger for PVAm/silica than for PVFA/silica, which corresponds to the observed higher swelling capacity of this polyelectrolyte material. Furthermore, the swelling behavior of the hybrid hydrogels was quantitatively described in terms of free swell capacity, centrifuge-retention capacity, adsorption against pressure, and free swell rate as compared with values of the corresponding copolymer hydrogels. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 3144–3152, 2002