Characterization and improved solar light activity of vanadium doped TiO2/diatomite hybrid catalysts

Abstract V-doped TiO 2 /diatomite composite photocatalysts with different vanadium concentrations were synthesized by a modified sol–gel method. The diatomite was responsible for the well dispersion of TiO 2 nanoparticles on the matrix and consequently inhibited the agglomeration. V-TiO 2 /diatomite hybrids showed red shift in TiO 2 absorption edge with enhanced absorption intensity. Most importantly, the dopant energy levels were formed in the TiO 2 bandgap due to V 4+ ions substituted to Ti 4+ sites. The 0.5% V-TiO 2 /diatomite photocatalyst displayed narrower bandgap (2.95 eV) compared to undoped sample (3.13 eV) and other doped samples (3.05 eV) with higher doping concentration. The photocatalytic activities of V doped TiO 2 /diatomite samples for the degradation of Rhodamine B under stimulated solar light illumination were significantly improved compared with the undoped sample. In our case, V 4+ ions incorporated in TiO 2 lattice were responsible for increased visible-light absorption and electron transfer to oxygen molecules adsorbed on the surface of TiO 2 to produce superoxide radicals O 2 – , while V 5+ species presented on the surface of TiO 2 particles in the form of V 2 O 5 contributed to e – –h + separation. In addition, due to the combination of diatomite as support, this hybrid photocatalyst could be separated from solution quickly by natural settlement and exhibited good reusability.