Synthesis and Properties of Polybenzoxazole Copolymers Having Non Linear Units

A series of poly(hyroxyamide)s (PHAs) was prepared by direct polycondensation reaction of 4,4′-(2,3-pyridinedioxy) dibenzoic acid and/or isophthalic acid with 3,3′-dihydroxybenzidine. The yield percentages of the products were high, and the inherent viscosities of the polymer in DMAc solution at 35℃ were 0.31-0.59 dL/g. All PHA polymers were found to be soluble in polar aprotic solvents such as DMAc, DMSO, NMP, and DMF. On the other hand, LiCl was required to dissolve IPHA-1 in aprotic solvents. Poly(benzoxazole)s (PBOs) were partially soluble in conc-H2SO4; IPBO-4, -5, and -6 were partially soluble in NMP only when LiCl was added to the solution, and the solution was heated. The PBO polymers showed a maximum weight loss in the temperature range of 654-680℃, and the char yields at 900℃ under nitrogen atmosphere exceeded 63%.