Testing of typical spacecraft materials in a simulated substorm environment

The test specimens were spacecraft paints, silvered Teflon, thermal blankets, and solar array segments. The samples, ranging in size from 300 to 1000 sq cm were exposed to monoenergetic electron energies from 2 to 20 keV at a current density of 1 NA/sq cm. The samples generally behaved as capacitors with strong voltage gradient at their edges. The charging characteristics of the silvered Teflon, Kapton, and solar cell covers were controlled by the secondary emission characteristics. Insulators that did not discharge were the spacecraft paints and the quartz fiber cloth thermal blanket sample. All other samples did experience discharges when the surface voltage reached -8 to -16kV. The discharges were photographed. The breakdown voltage for each sample was determined and the average energy lost in the discharge was computed.