Proton irradiation and characterization of additively manufactured 304L stainless steels

Abstract Irradiations were performed with 1.5 MeV protons to 0.6 dpa at 40–150 °C on additively manufactured (AM) 304L stainless steel and the changes in microstructure and mechanical behavior after irradiation were compared to wrought 304L stainless steel. All microstructural and hardness results after irradiation suggest the samples evolve toward a similar state, despite significant differences in the unirradiated microstructures and hardness values. A TEM and nanoindentation-based investigation of before and after proton irradiation at 40–150 °C is presented. Results are interpreted in terms of initial dislocation content, dislocation structures, and microstructural and chemical homogeneity.