Dramatic enhancement of near-infrared intersubband absorption in c-plane AlInN/GaN superlattices

We report substantial improvement of near-infrared (2–2.6 μm) intersubband absorption in c-plane AlInN/GaN superlattices grown by molecular beam epitaxy. Progress was obtained through optimization of AlInN growth conditions using an AlInN growth rate of 0.9-nm/min at substrate temperature of 550 °C, as well as by judiciously placing the charge into two delta-doping sheets. Structural characterization suggests that AlInN crystal quality is enhanced and interface roughness is reduced. Importantly, near-infrared absorption data indicate that the optical quality of the AlInN/GaN superlattices is now comparable with that of AlN/GaN superlattices designed to exploit near-infrared intersubband transitions.