Effects of Bi nonstoichiometry in (Bi0.5+xNa)TiO3 ceramics
2011
Effects of Bi nonstoichiometry on (Bi0.5+xNa)TiO3 (BNT) ceramics were investigated at x=−1–+2 mol % of Bi0.5 covering Bi deficiency and excess. At all compositions, rhombohedrally symmetric BNT perovskite formed without secondary phases. Increasing x caused smaller grains. Higher piezoelectric coefficient (d33) but lower depolarization temperature (Td) occurred at Bi excess than at Bi deficiency and vice versa. Leakage current at room temperature decreased with decreasing x. Electrical conductivity of the stoichiometric BNT (x=0) from 700 to 900 °C increased with decreasing partial oxygen pressure from 1 to 10−5 atm suggesting n-type conductivity at elevated temperatures.