Effects of Heat-Treatment on Photoluminescence Spectra and Photocatalytic Properties of Solution-Combusted ZnO Nanopowders

: ZnO nanopowders were prepared by a solution combustion method (SCM). The SCM ZnO nanopowders were heat-treated at 200, 400, 500, or 700 °C for 30 min in air and the photoluminescence (PL) of the nanopowders was evaluated. Two strong PL emission peaks are generally recognized as the unique PL signature of ZnO, one is from the band-edge emission and the other corresponds to green emission. The green emission is derived from crystalline defects, and is a critical obstacle for the electrooptical applications of ZnO. Surprisingly, the PL spectra of the SCM ZnO powders showed a single sharp peak near 390 nm. Furthermore, the intensity of this blue emission doubled when the synthesized ZnO powder was heat-treated at 400 °C. The green emission appeared for the sample treated at 500 °C, and was the highest for that treated at 700 °C. To comfirm the photocatalytic activity of the ZnO powder heat-treated at 400 °C, the removal of Ag ions from a used photofilm developer was evaluated, with complete removal within 10 min. The removal of the Ag ions by the ZnO powder heat-treated at 400 °C was more than two orders of magnitude faster than that achieved with the SCM ZnO powder. The relation between PL and photocatalytic activity was explained in terms of recombination of the photogenerated electrons. These results might be very useful for highly efficient photocatalyst applications.