Development of the paramagnetic RABiTS tapes for coated conductors
2014
RABiTS production process was developed for tapes from Ni-W alloys with W content in the range of 4-10.5 at.%. Tapes' composition, structure and magnetic properties were investigated. High purity Ni-W ingots were smelted and tapes with thickness of 0.06-0.09 mm and various total accumulated deformations in the range of 90-99.2% were fabricated. Texture quality dependence on accumulated deformation in the tapes with W various content was studied. X-ray analysis data including pole figures show that high quality cube texture can be formed in the tapes with W content up to 9 at.% inclusive, but not formed in the tapes with 10.5 at.%. According Curie temperature values and saturation magnetization measurements of alloys with W content more than 8 at.% are paramagnetic at liquid nitrogen temperature. Summarizing it can be stated that RABiTS tapes with 8-9 at.% W content have optimal combination of structure and magnetic properties for using in coated conductors.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
4
References
3
Citations
NaN
KQI