Evaluation on Hydrogen Embrittlement of 5 Types of High Strength Dual Phase Steels by Small Punch Test

Abstract - The hydrogen embrittlement degree of 5 type high strength DP steel charged with hydrogen by electrochemical method was evaluated by small punch test(SP test). After SP test, SP absorbed energy was remarkably decreased from 363 kgf-mm to 209 kgf-mm with increasing hydrogen charging time from 5hr to 50hr at DP5 specimen under the 200 mA/cm 2 current density condition. It was investigated that the decrease of hydrogen charging amount and SP absorbed energy according to the increase of current density and hydrogen charging time had a linear relationship. And it also investigated that the change of bulb height appeared by the SP test was decreased from 1.79mm to 1.59mm wit h the hydrogen charging conditions. It was supposed that it could be used as indicator of the evaluation of hydrogen embrittlement because of the similar trend of the formal results of SP absorbed energy. From the SEM observation of fracture area by crack in bulb, the morphology of fracture surface according to increasement of the hydrogen charging amount was varied with the cleavage mode.Key words : hydrogen embrittlement, small punch test, SP absorbed energy, cleavage mode