Step structure on the fivefold Al–Pd–Mn quasicrystal surface, and on related surfaces
2005
We compare step morphologies on surfaces of Al-rich metallic alloys, both quasicrystalline and crystalline. We present evidence that the large-scale step structure observed on Al-rich quasicrystals after quenching to room temperature reflects equilibrium structure at an elevated temperature. These steps are relatively rough, i.e., have high diffusivity, compared to those on crystalline surfaces. For the fivefold quasicrystal surface, step diffusivity increases as step height decreases, but this trend is not obeyed in a broader comparison between quasicrystals and crystals. On a shorter scale, the steps on Al-rich alloys tend to exhibit local facets (short linear segments), with different facet lengths, a feature which could develop during quenching to room temperature. Facets are shortest and most difficult to identify for the fivefold quasicrystal surface.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
42
References
21
Citations
NaN
KQI