Tear and decohesion of bovine pericardial tissue.

Abstract The aim of this study was to evaluate quantitatively the fracture—by tear and delamination—of bovine pericardium tissues which are usually employed for the manufacture of bioprosthetic valves. A large number of samples (77) were tested in root-to-apex and circumferential directions, according to a standardised tear test (ASTM D 1938). Before performing the tear test, some samples were subjected to 1000 cycles of fatigue to a maximum stress of 3 MPa. Fracture toughness of tearing and delamination were computed by following a simple fracture model. The study showed significantly lower values of delamination toughness compared with tear delamination. Moreover, tear forces were different in each test direction, revealing a clear orthotropic behaviour. All these results, as well as the testing procedure, could be of value for future research in the physiological function of pericardium tissues and clinical applications.