Three-dimensional graphitic mesoporous carbon-doped carbon felt bioanodes enables high electric current production in microbial fuel cells

Abstract Microbial fuel cells (MFCs) represent a new approach that can simultaneously enhance the treatment of waste streams and generate electricity. Although MFCs represent a promising technology for renewable energy production, they have not been successfully scaled-up mainly due to the relatively-low electricity generation and high cost associated with MFCs operation. Here, we investigated whether graphitic mesoporous carbon (GMC) decoration of carbon felt would improve the conductivity and biocompatibility of carbon felt anodes, leading to higher biomass attachment and electricity generation in MFCs fed with an organic substrate. To test this hypothesis, we applied 3 different GMC loading (i.e., 2, 5, and 10 mg/cm2 of anode surface area) in MFCs compared to control MFCs (with pristine carbon felt electrodes). We observed that the internal resistances of modified anodes with GMC were 1.2–2.3-order of magnitude less than pristine carbon felt anode, leading to maximum power densities of 70.3, 33.3, and 9.8 mW/m2 for 10, 5, and 2 mg/cm2-doped anode, respectively compared to only 3.8 mW/m2 for the untreated carbon felt. High-throughput sequencing revealed that increasing the GMC loading rate was associated with enriching more robust anode-respiring bacteria (ARB) biofilm community. These results demonstrate that 3-D GMC-doped carbon felt anodes could be a potential alternative to other expensive metal-based electrodes for achieving high electric current densities in MFCs fed with organic substrates, such as wastewater. Most importantly, high electron transfer capability, strong chemical stability, low cost, and excellent mechanical strength of 3-D GMC-doped carbon felt open up new opportunities for scaling-up of MFCs using cheap and high-performance anodes.