Laser Light and X-Ray Diffraction Studies of Oriented Isotactic Polypropylene (iPP) Prepared by Temperature Slope Crystallization

Isotactic polypropylene (iPP) film was melt-crystallized in a temperature gradient. The iPP film showed well oriented α- and β-crystalline textures along the gradient. The crystalline structure, phase transition boundary and lamellar twisting were examined by X-ray diffraction and laser light diffraction (LLD). On the α-β boundary, LLD shows a sharp streak perpendicular to the boundary, where the a-axis of the β-crystal is oriented perpendicular to the temperature gradient. Apart from the boundary, the a-axis of the β-crystal becomes parallel to the gradient. The β-crystal shows lamellar twisting with a pitch of 200 μm at room temperature. When heated the β-crystal, the lamellar distance of 295A at room temperature decreases to 285A at 80–100°C and then increases to more than 300A above 120°C. During the heating, the value of the twist period increases from 200 to 210 μm at 90–100°C, and then to above 224 μm at 140°C. The increase of the twist period is related to the increasing crystalline thickness of t...