C/V 흑연주철(黑鉛鑄鐵)의 조직(組織)과 기계적성질(機械的性質)에 미치는 Sb첨가효과(添加效果)

【In order to study the infuence of Sb addition on the compacted vermicular graphite cast iron(C/V) and gray cast iron(GC), these specimen which had different Sb content(0-0, 1wt.%) were prepared. these specimen were tested for microstructure and mechanical properties. The result from this study are as follows. For C/V and GC, the microstructure of graphite appeared to be finer with increasing Sb content more than 0.06wt.% Ferrite disappeared from the matrix with addition of Sb more than 0.06wt.% in GC and more than 0.08wt.% in C/V. The size of the eutectic cell in GC was 4.5 to 7 times larger than that in C/V, but the decreasing tendancy of its size was more remarkable in GC than in C/V with increasing Sb content. The abrasion speed corresponding to the maximum amount of abrasion in the nabrasion test was found to be 1.37m/sec. GC sample weared 3.6 to 21 times faster than those of C/V did. the amount of abrasion demeased remarkably with Sb addition, and the abrasion rate was constant with Sb content over 0.04wt.%】