Effect of Hot Forging and Different Cooling Rates on the Microstructure, Mechanical Properties of Carbon Steel Containing 0.8 and 1.2Al

Two alloys of steel containing nominally 0.45C-1.0Si-2.0Mn-0.8Al and 1.2Al were cast in open air induction furnace. Dilatation testing was carried out to recognize the effect on Aluminum on the different critically transformation temperatures. The alloys were hot forged at 1200°C and then subjected to different cooling rates. Mechanical testing was carried out at room temperature. Optical and SEM microstructure were observed. X-ray diffraction was conducted to observe the microstructure constituents.