Defects and nanocluster engineering in MgO

The optical properties of MgO crystals are known to change after introduction of nanosize metal precipitates. In this work the formation of metallic nanoclusters in the presence of nanosize rectangular shaped cavities was studied. The rectangular cavities were formed by 30 keV He+ implantation followed by 1273 K annealing. The formation of cavities and their location was established by Positron Beam Analysis (PBA). The rectangular shape and their alignment in (100) direction was observed by X-TEM. Subsequently, the samples were implanted with 600 keV Ag and 1000 keV Au in order to introduce the metal ions in the vicinity of the cavities. The samples were then annealed to provide the formation of nanoclusters. The evolution of the implantation induced defects was monitored by PBA. The optical properties were studied by light absorption measurements.