Structural, magnetic and GMR properties of FeCo(Cu)/Cu magnetic multilayers electrodeposited at high cathode potentials of the magnetic layer

Structural, magnetic and giant magnetoresistance properties of the electrochemically deposited FeCo(Cu)/Cu multilayers at the various cathode potentials for magnetic layers were investigated. The cathode potentials were 1.8, 2.0, 2.5 and 2.8 V for magnetic layers and 0.3 V for non-magnetic layers with respect to a saturated calomel electrode. The multilayers have a face-centred-cubic structure. The obtained composition was found to be close the nominal composition at 2.8 V cathode potential. The highest giant magnetoresistance value (16.50 %) was obtained in the multilayer produced at 1.8 V. The highest sensitivity was found in the multilayer produced at 1.8 and 2.8 V.