Effect of Al2O3 ceramic binder on mechanical and microstructure properties of spark plasma sintered WC-Co cermets

Abstract This study investigates how the partial replacement of Co with Al 2 O 3 ceramic binder has an effect on the sintering behaviour, microstructure, and final mechanical properties of WC-Co cermets via spark plasma sintering. To examine this, three batches (WC-6 wt%Co, WC-3 wt%Co-3 wt%Al 2 O 3, and WC-6 wt%Al 2 O 3 ) were mixed through high energy ball mill, and sintering was carried out at temperatures of 1350 °C and 1600 °C. The results showed nearly full dense WC-Co cermets at different temperatures. It was shown that WC-6 wt%Al 2 O 3 , in comparison to reference WC-6 wt%Co cermet, not only led to the rise in sintering temperature from 1350 °C to 1600 °C, but also reduced its strength and toughness. But replacing some part of Co with alumina (WC-3 wt%Co-3 wt%Al 2 O 3 ) exhibited the combination of high strength (1095 MPa), hardness (17.62 GPa), and fracture toughness (19.46 MPa·m 1/2 ).