Investigation of Coke Formation in Dry Methane Reforming over Nickel-based Monolithic Catalysts

Coking accumulations via dry methane reforming (DMR) over 10NAM monolithic catalyst and pelletized catalyst was investigated. 10NAM catalyst was synthesized and coated on a wall of monolithic reactor. Pelletized catalyst of 10NAM was also prepared for the comparison. Consequently, catalyst was characterized by BET, and . The catalytic reaction was undergone at under atmospheric pressure and to reactant ratio of 1:2. The coking formation over spent catalyst was then carried out in the hydrogen flow using temperature programmed technique (TPH). According to the results, DMR over 10NAM monolithic catalyst exhibits a minimized coking formation comparing to the use of pelletized catalyst. This could be attributed to a prominent heat transfer efficiency of the monolithic catalyst.