Radiative transitions in stacked type-II ZnMgTe quantum dots embedded in ZnSe

Sub-monolayer quantities of Mg are introduced in multilayer stacked ZnMgTe quantum dots (QDs) embedded in ZnSe barriers in order to reduce the hole confinement energy by controlling the bandgaps and band-offsets of ZnTe/ZnSe system having type-II band alignment. The photoluminescence (PL) emission from such ZnMgTe/ZnSe QD structure is found to be a broad band centered at 2.35 eV. The higher energy side of the PL band shows a larger blue-shift with increasing excitation intensity and a faster life-time decay due to a greater contribution of the emission from the smaller size dots and the isoelectronic bound excitons. It is found that the characteristic decay time of the PL evolves along the band with a value of 129 ns at 2.18 eV to 19 ns at 2.53 eV. The temperature dependent PL emission is controlled by two thermally activated processes: ionization of electrons away from QD state to the barrier (EA1 ∼ 3 meV) by breaking the type-II excitons and thermal escape of the holes from the ground state to the barri...