Synthesis and electrochromic properties of polybismaleimides containing triphenylamine units

The bismaleimide (BMI) monomer containing triphenylamine was prepared firstly. Then BMI was reacted with different diamines by Michael addition to obtain prepolymers, respectively. Finally, polyimides (PIs) were obtained through melting procedure. The effects of the structure of BMI moiety and thermal curing condition on thermal stability of PIs were studied by thermogravimetric analysis. PIs have excellent processing properties for film casting. Cyclic voltammetry of PI films was carried out on an indium-doped tin oxide-coated glass substrate. Results which exhibit two reversible oxidations at 0.71–0.78 and 1.06–1.16 V vs Ag/AgCl. The electrochromic performance was investigated by spectroelectrochemical methods. These anodically coloring polymer films not only showed good electrochromic properties but also exhibited high optical contrast ratio of transmittance with a color changing from yellow to green. After 100 cyclic switches, the polymer films still retained excellent redox and electrochromic activity.