Size Effect on the Mechanical Properties of CF Winding Composite

Mechanical properties of filament winding composites are usually tested by NOL ring samples. Few people have studied the size effect of winding composite samples on the testing result of mechanical property. In this research, winding composite thickness, diameter, and geometry of NOL ring samples were prepared to investigate the size effect on the mechanical strength of carbon fiber (CF) winding composite. The CF T700, T1000, M40, and M50 were adopted for the winding composite, while the matrix was epoxy resin. Test results show that the tensile strength and ILSS of composites decreases monotonically with an increase of thickness from 1 mm to 4 mm. The mechanical strength of composite samples increases monotonically with the increase in diameter from 100 mm to 189 mm. The mechanical strength of composite samples with two flat sides are higher than those of cyclic annular samples.