Preparation of Silver Nanoparticles Coated ZnO/Fe3O4 Composites Using Chemical Reduction Method for Sensitive Detection of Uric Acid via Surface-enhanced Raman Spectroscopy

2019 
Abstract In this study, silver nanostructures decorated magnetic nanoparticles for surface-enhanced Raman scattering (SERS) measurements were prepared via heat induced catalytic activity of ZnO nanostructures. The ZnO/Fe 3 O 4 composite was first prepared by dispersing pre-formed magnetic nanoparticles into alkaline zinc nitrate solutions. After annealing of the precipitates, the formed ZnO/Fe 3 O 4 composites were successfully decorated with silver nanostructures by dispersing the composites into silver nitrate/ethylene glycol solution at 95 °C in water bath. To find the optimal condition when preparing Ag/ZnO/Fe 3 O 4 composites for SERS measurements, factors such as reaction time and concentration of silver nitrate were studied. Results indicated that the formation of silver nanoparticles (AgNPs) on ZnO/Fe 3 O 4 was significantly improved with the assistance of ZnO. The concentration of silver nitrate and reaction time affected the morphologies and sizes of the formed composites and optimal condition in preparation of the composites for SERS measurement was found using 100 mM of silver nitrate with a reaction time of 20 min. Under optimized conditions, the obtained SERS intensities were highly reproducible. The substrates were applied for quantitative analysis of uric acid in aqueous solution and a linear response for concentrations up to 10 μM was obtained. Successful application of these prepared composites to determine uric acid in urine sample without any pretreatment of the urine sample was done.
    • Correction
    • Source
    • Cite
    • Save
    • Machine Reading By IdeaReader
    44
    References
    30
    Citations
    NaN
    KQI
    []