Synthesis and characterization of F-doped Cs{sub 0.33}WO{sub 3−x}F{sub x} particles with improved near infrared shielding ability
2015
F-doped Cs{sub 0.33}WO{sub 3−x}F{sub x} particles were successfully synthesized by the hydrothermal method with hydrofluoric acid as fluorine source, and a new kind of heat insulating films were prepared from dispersion of Cs{sub 0.33}WO{sub 3−x}F{sub x} nanoparticles in polyvinyl alcohol (PVA) aqueous solution. The effects of F doping on the crystal structure and morphology of Cs{sub 0.33}WO{sub 3−x}F{sub x} particles as well as the near-infrared (NIR) shielding ability and heat insulation properties of Cs{sub 0.33}WO{sub 3−x}F{sub x} films were investigated. The results indicated that HF acid addition could promote the formation of rod-like Cs{sub 0.33}WO{sub 3−x}F{sub x} particles during hydrothermal synthesis and increase the yield of Cs{sub 0.33}WO{sub 3−x}F{sub x} powders. Moreover, the as-prepared films from dispersion solution of Cs{sub 0.33}WO{sub 3−x}F{sub x} particles exhibited higher near-infrared (NIR) shielding ability and heat insulating properties than that of the undoped Cs{sub 0.33}WO{sub 3} film. Particularly, the as-prepared Cs{sub 0.33}WO{sub 3−x}F{sub x} sample with F/W (molar ratio)=0.45 showed best NIR shielding ability and transparent heat insulating performance. The formation mechanism of nanorod-like particles and the effects of F doping on the properties of Cs{sub 0.33}WO{sub 3−x}F{sub x} products were discussed. - Graphical abstract: F-doped Cs{sub 0.33}WO{sub 3−x}F{sub x} particles were successfully synthesizedmore » by the hydrothermal method with hydrofluoric acid as fluorine source. HF acid addition in the precursor solution could increase the yield of Cs{sub 0.33}WO{sub 3−x}F{sub x} powders and promote the formation of rod-like Cs{sub 0.33}WO{sub 3−x}F{sub x} particles. Moreover, the as-prepared Cs{sub 0.33}WO{sub 3−x}F{sub x} films from dispersion solution of Cs{sub 0.33}WO{sub 3−x}F{sub x} particles exhibited higher near-infrared (NIR) shielding ability and heat insulating properties than that of the undoped Cs{sub x}WO{sub 3} film. Particularly, the as-prepared Cs{sub 0.33}WO{sub 3−x}F{sub x} sample with F/W (molar ratio)=0.45 showed best NIR shielding ability and transparent heat insulating performance. - Highlights: • F-doped Cs{sub 0.33}WO{sub 3−x}F{sub x} powders were successfully synthesized by the hydrothermal method. • HF acid addition could promote the formation of rod-like Cs{sub 0.33}WO{sub 3−x}F{sub x} particles. • The near infrared shielding ability of Cs{sub 0.33}WO{sub 3} was further improved by F doping. • The Cs{sub 0.33}WO{sub 3−x}F{sub x} films exhibited higher transparent heat insulation than Cs{sub 0.33}WO{sub 3}.« less
- Correction
- Cite
- Save
- Machine Reading By IdeaReader
0
References
0
Citations
NaN
KQI