Investigation of kinetic recovery process in low dose neutron-irradiated nuclear graphite by thermal annealing

ABSTRACTTo investigate the kinetic recovery process of low dose neutron-irradiated graphite, nuclear-grade isotropic graphite IG-110U and ETP-10 were neutron irradiated using the JMTR up to 1.38 × 1023 n/m2 (En > 1 MeV) at ~473 K. In-situ measurement of macroscopic length was conducted during the isothermal and isochronal annealing process from room temperature up to 1673 K. From room temperature to 773 K for IG-110U, and to 1023 K for ETP-10, macroscopic lengths, lattice parameters, and unit cell volumes of both specimens recovered to their pre-irradiation values, and this recovery process subdivided into two stages. The activation energies of macroscopic volume recovery at 523–673 K and 673–773 K were determined to be ~0.22 eV and ~0.57 eV for IG-110U, respectively; ~0.13 eV and ~2.59 eV at 523–923 K and 923–1023 K for ETP-10, respectively. The migration of not only single interstitials but also interstitials dissociated from submicroscopic interstitial groups along basal planes followed by vacancy-inte...