Crystal structure and electrical property comparisons of epitaxial Pb(Zr,Ti)O3 thick films grown on (100)CaF2 and (100)SrTiO3 substrates

Epitaxial Pb(Zr,Ti)O3 (PZT) thick films of 2.0–3.0 μm thickness were grown at 600 °C on (100)cSrRuO3∥(100)SrTiO3 and (100)cSrRuO3∥(100)LaNiO3∥(100)CaF2 substrates by pulsed-metal organic chemical vapor deposition. All films showed (100) and/or (001) orientations with tetragonal symmetry. It was found that there is an almost linear relationship between the estimated thermal strain from the deposition temperature to the Curie temperature and the volume fraction of (001) orientation in the mixture of (100) and (001) orientations for the films on both substrates. Consequently, the perfectly (001)-oriented, i.e., polar-axis-oriented, PZT thick films were obtained on CaF2 with the Zr/(Zr+Ti) ratio from 0.20 to 0.40. Moreover, the lattice parameter of a- and c-axes and their ratio (c/a) of those polar-axis-oriented films were almost the same as the reported data for the powder, suggesting that the large strain is not remaining in those films. The relative dielectric constant (er) of the polar-axis-oriented Pb(Zr...