Facile preparation of macro-mesoporous zirconium titanate monoliths via a sol–gel reaction accompanied by phase separation
2019
Macro-mesoporous zirconium titanate monoliths have been successfully prepared via a sol–gel process accompanied by phase separation, with poly(ethylene oxide) (PEO) as a phase separation inducer and N -methylformamide (NFA) as a gelation accelerator. The size and morphology of macropores are controlled by the PEO and NFA amount. By choosing appropriate starting composition, the co-continuous structure could be obtained. The as-dried gel is amorphous, the pore size is in the range of 0.05–0.5 μm, the porosity is 46%, and the surface area is 111 m 2 /g. After heat treatment at 500 °C, the gel transforms into the phase ZrTiO 4 , the macropore diameter decreases slightly, the porosity increases to 63%, and the surface area decreases to 40 m 2 /g. Moreover, the macroporous structure is well maintained, and the skeleton becomes dense and smooth. The samples have macropores, mesopores, and micropores before and after heat treatment.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
34
References
1
Citations
NaN
KQI