Benzoyl Halide as Alternative Precursor for Synthesis of Lead Free Double Perovskite Cs3Bi2Br9 Nanocrystals

Ternary bismuth halides are interesting functional materials closely related to Pb halide perovskite photovoltaic material, and are widely sought after due to reduced toxicity of Bi compared to Pb. There are several reports on synthesis of Cs(3)Bi(2)Br9 nanocrystals (NCs) due to its being relatively stable compared to lead perovskite. Cs(3)Bi(2)Br9 nanocrystals have been synthesised using benzoyl bromide as an precursor using hot injection process at two different temperatures of 120 degrees C and 160 degrees C. Samples have been characterized for its structural, optical, microstructural and luminescent properties using X-ray diffraction, (XRD) UV-Vis spectroscopy, high resolution transmission electron microscopy and photoluminescent spectroscopy. XRD showed formation of Cs(3)Bi(2)Br9 phase with mono-crystalline structure. UV-Vis showed two types of band gap in the visible region which shows that the material can be used for photovoltaic applications. HRTEM confined the particles to be composed of nanocrystals with 5 nm particles in the samples grown at 120 degrees C and it the particles joined together yield various structures composed of nanoparticles. The time resolved photoluminescence shows average life times of 3.067 ns and 4.761 ns for samples grown at two different temperatures. To the best of our knowledge, this is the first report where benzoyl halide has been used as alternative precursor for the synthesis of lead free double perovskite Cs(3)Bi(2)Br9 nanocrystals which have many applications.