The Effect of Composition and Microstructure on Corrosion Behavior in SST of Zn-Al-Mg Galvanized Steel Sheet
2013
Z11A3M, Z6A3M, Z1.6A1.6M, Z1A1M and Z1M coating samples were prepared in HDPS by traditional continuous hot dipping method. The microstructure, element distribution and phase was analyzed by SEM, EPMA and XRD. The corrosion resistance was checked in SST. The result was, MgZn2 and eutectic could be found in all ZAM coating. The ZAM coatings showed excellent corrosion resistance in SST than GI. The corrosion resistance was 4.1 to 11 times of GI. There was no strong relativity between alloy composition and corrosion resistance due to Mg enrichment on the surface of coating. Edge-unsealed ZAM samples showed good corrosion resistance than edge-sealed sample.
Keywords: