Preparation of MnCo/MCM-41 catalysts with high performance for chlorobenzene combustion

Abstract MCM-41 was synthesized by a soft template technique. The specific surface area and pore volume of the MCM-41 were 805.9 m 2 /g and 0.795 cm 3 /g, respectively. MCM-41-supported manganese and cobalt oxide catalysts were prepared by an impregnation method. The energy dispersive X-ray spectroscopy clearly confirmed the existence of Mn, Co, and O, which indicated the successful loading of the active components on the surface of MCM-41. The structure and function of the catalysts were changed by modulating the molar ratio of manganese to cobalt. The 10%MnCo(6:1)/MCM-41 (Mn/Co molar ratio is 6:1) catalyst displayed the best catalytic activity according to the activity evaluation experiments, and chlorobenzene (1000 ppm) was totally decomposed at 270 °C. The high activity correlated with a high dispersion of the oxides and was attributed to the exposure of more active sites, which was demonstrated by X-ray diffraction and high-resolution transmission electron microscopy. The strong interactions between MnO 2 , Co 3 O 4 , MnCoO x , and MCM-41 indicated that cobalt promoted the redox cycles of the manganese system. The bimetal-oxide-based catalyst showed better catalytic activity than that of the single metal oxide catalysts, which was further confirmed by H 2 temperature-programmed reduction. Chlorobenzene temperature-programmed desorption results showed that 10%MnCo(6:1)/MCM-41 had higher adsorption strength for chlorobenzene than that of single metal catalysts. And stronger adsorption was beneficial for combustion of chlorobenzene. Furthermore, 10%MnCo(6:1)/MCM-41 was not deactivated during a continuous reaction for 1000 h at 260 °C and displayed good resistance to water and benzene, which indicated that the catalyst could be used in a wide range of applications.