Effect of NCO/OH ratio and Ce‐Zr nanoparticles on the thermo‐mechanical properties of hyperbranched polyurethane urea coatings

The present study describes the effect of NCO/OH ratio and addition of Cerium (Ce)-Zirconium (Zr) mixed oxide nanoparticles on the properties of Hyperbranched Polyurethane Urea (HBPUU) Coatings. Initially a hydroxyl terminated hyperbranched polymer (HTBP) was synthesized through A3 + CB2 approach. The HTBP and Ce-Zr nanopowder dispersed HTBP, both were reacted with hexamethylene diisocyanate (HDI) separately; at various NCO/OH eq. ratios to get different NCO terminated HBPU and HBPU/Ce-Zr hybrid prepolymers. These prepolymers were used for the preparation of HBPUU and HBPUU/Ce-Zr hybrid coating films through moisture curing. The techniques such as 1H NMR, 13C NMR, FT-IR, and XRD have been used for structural information while Dynamic mechanical and thermal analyzer (DMTA), Thermogravimetric analysis (TGA) and Universal testing machine (UTM) have been used for evaluation of thermo-mechanical properties. The combined spectroscopic investigations results indicate the formation of HBPUU network with a degree of branching of 76% while FT-IR deconvolution results indicates the formation of more hydrogen bonded structure with increasing NCO/OH ratio. The XRD and FT-IR studies confirm the presence of Ce-Zr mixed nanoparticles in the HBPUU hybrids. As per TGA and DMTA analysis the thermal stability, char residue, storage modulus (E', material stiffness) and glass transition temperature (Tg), increases with increasing NCO/OH ratio and Ce-Zr nanoparticle loading in HBPUU coatings. In general, UTM data suggest that the tensile strength increases and per cent elongation at break decreases with increasing the NCO/OH ratio and addition level of nanoparticles in HBPUU coatings. Copyright © 2009 John Wiley & Sons, Ltd.