Erosion wear behaviour of plasma sprayed NiCrSiB/Al2O3 composite coating

Abstract In this work, 60 wt.% NiCrSiB–40 wt.% Al 2 O 3 composite coating was produced on AISI 304 substrate material using the atmospheric plasma spraying technique. The coating surface has been characterised using a scanning electron microscope (SEM), optical microscope and X-ray diffractometer (XRD). The microhardness, porosity, density and surface roughness of the coating were measured. The adhesion strength of the coating was measured using pull off adhesion tester. The erosion behaviour of plasma sprayed coating was studied at 450 °C using hot air jet erosion testing machine. The erosion rate of coated and uncoated samples was evaluated at 30° and 90° erodent impact angles. The SEM images of the eroded samples were taken to analyse the erosion mechanism. The test results reveal that the coating protects the substrate at both 30° and 90° impact angles.