A Dual Active-Passive Coating with Intumescent and Fire-Retardant Properties Based on High Molecular Weight Tannins

2021 
In this study, the tannins extracted from the Pinus radiata bark were used to develop an active–passive dual paint scheme with intumescent (IN) and fire-resistant (FR) behaviors. The properties of the coating were observed to depend on the concentration of high-molecular-weight tannins (H-MWT) incorporated into the formulation. At high concentrations (13% w/w), the coating exhibits fire-retardant properties due to the generation of a carbonaceous layer; however, at low concentrations (2.5% w/w), it generates an intumescent effect due to the formation of a carbonaceous foam layer. The dual IN–FR scheme was evaluated against fire by flame advance tests, carbonization index, mass loss, and intumescent effect, and was also compared to a commercial coating. The dual scheme presented good mechanical properties with a pull-off adhesion value of 0.76 MPa and an abrasion index of 54.7% at 1000 cycles, when using a coating with a high solid content (>60%) and the same thickness as those of the commercial coatings. The results of the fire resistance test indicate that the dual scheme generates a protective effect for wood and metal, with an excellent performance that is comparable to that of a commercial intumescent coating.
    • Correction
    • Source
    • Cite
    • Save
    • Machine Reading By IdeaReader
    35
    References
    2
    Citations
    NaN
    KQI
    []