High temperature structural study of Gd-doped ceria by synchrotron X-ray diffraction (673 K ≤ T ≤ 1073 K).

The crystallographic features of Gd-doped ceria were investigated at the operating temperature of solid oxides fuel cells, where these materials are used as solid electrolytes. (Ce1–xGdx)O2-x/2 samples (x = 0.1, 0.3, 0.5, 0.7) were prepared by coprecipitation of mixed oxalates, treated at 1473 K in air, and analyzed by synchrotron X-ray diffraction in the temperature range 673 K ≤ T ≤ 1073 K at the Elettra synchrotron radiation facility located in Trieste, Italy. In the whole temperature span a boundary was found at x ∼ 0.2 between a CeO2-based solid solution (for x ≤ 0.2) and a structure where Gd2O3 microdomains grow within the CeO2 matrix, taking advantage of the similarity between Gd3+ and Ce4+ sizes; the existence of the boundary at x ∼ 0.2 was confirmed also by measurements of ionic conductivity performed by impedance spectroscopy. Similar to what observed at room temperature, the trend of the cell parameter shows the presence of a maximum; with increasing temperature, the composition corresponding t...