Adhesion and friction properties of polymer brushes: fluoro versus nonfluoro polymer brushes at varying thickness.

A series of different thicknesses of fluoro poly(2,2,2-trifluoroethyl methacrylate) and its analogous nonfluoro poly(ethyl methacrylate) polymer brushes were prepared via surface-initiated ATRP (SI-ATRP) on Si(111) surfaces. The thiol-yne click reaction was used to immobilize the SI-ATRP initiator with a high surface coverage, in order to achieve denser polymer brushes (grafting density from ∼0.1 to 0.8 chains/nm2). All polymer brushes were characterized by static water contact angle measurements, infrared absorption reflection spectroscopy, and X-ray photoelectron spectroscopy. Adhesion and friction force measurements were conducted with silica colloidal probe atomic force microscopy (CP-AFM) under ambient and dry (argon) conditions. The fluoro poly(2,2,2-trifluoroethyl methacrylate) polymer showed a decrease in adhesion and friction with increasing thickness. The analogous nonfluoro poly(ethyl methacrylate) polymer brushes showed high adhesion and friction under ambient conditions. Friction coefficients...