Effect of silty sand in formation water on CO2 corrosion behavior of carbon steel
2016
Abstract Corrosion behavior of carbon steel in CO 2 aqueous environment containing silty sand was investigated using corrosion mass loss method, scanning electron microscopy (SEM), energy diffraction spectrum (EDS), and various electrochemical measurements. The results show that the corrosion rate of carbon steel was obviously reduced due to the existence of silty sand. Silty sand promoted the rapid heterogeneous nucleation of corrosion product FeCO 3 and simultaneously decreased its grains growth. Silty sand mixed with corrosion product to form the outer layer of corrosion scale with high compactness, blocking the transport of ferrous ions and leading to the formation of the inner layer of corrosion scale without silty sand. The existence of silty sand in the outer layer of corrosion scale inhibited anodic and cathodic currents.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
37
References
15
Citations
NaN
KQI